氧化鋅行業用耐火材料 
推薦產品 
聯系我們 
| 類型Type | 材料名稱Material |
牌號 Brand |
最高使用溫度（℃）Mas opera-tional Temp | 110℃烘干后體積密度（g/ cm3）BULK Density after Drying at110℃(g/ cm3 |
化學成份 Cold Bending Strength(MPa) |
冷態抗折強度（MPa） Cold Crushing Strength(MPa) |
冷態抗折強度（MPa） Cold Crushing Strength(MPa) |
燒后線變化率（％）liner change afer finign （％） |
施工參考 （％）water usedcluring con-structlon（％） |
施工方法 constractionmethed |
使用部位 Position U sed |
||||||||||||||||||||||||||
| A|2O3 | Sio2 | 110℃×24h | 1110℃×3h | 1500℃×3h | 110℃×24h | 1110℃×3h | 1500℃×3h | 1100℃×3h | 1500℃×3h | ||||||||||||||||||||||||||||
|
剛玉質高強低水泥 Lightstrengthconund-um lowcement |
剛玉質高強低水泥耐火澆注料Hight strength corundum low cement refractory castable | G-17 | 1650 | ≥3.00 | ≥90 |
≤6 |
≥13 | ≥13 | ≥15 | ≥100 | ≥100 | ≥100 | ±0.30 | ±0.60 | 4.5-5.5 |
振動 Vibration |
大型水泥窯前窯口，噴煤管等部位及其它工業窯爐內襯Nosering of kiln outlet Coal injection pipes andLining of kiln | ||||||||||||||||||||
| 剛玉質高強低水泥耐火澆注料Hight strength corundum low cement refractory castable | G-18S | 1700 | ≥3.00 | ≥92 | ≤4 | ≥13 | ≥13 | ≥15 | ≥100 | ≥100 | ≥100 | ±0.30 | ±0.60 | 5-6 |
振動 Vibration |
大型水泥窯前窯口，噴煤管等部位及其它工業窯爐內襯Nosering of kiln outlet Coal injection pipes andLining of kiln | |||||||||||||||||||||
| 剛玉質高強低水泥耐火澆注料Hight strength corundum low cement refractory castable | G-18 | 1750 | ≥3.00 | ≥93 | ≤1 | ≥8 | ≥8 | ≥8 | ≥80 | ≥80 | ≥80 | ±0.3 | ±0.50 | 5.5-6.5 |
振動 Vibration |
振動同G—18S使用部位但使用溫度較高 Same as that of G-18,but operational temp.is much higher |
|||||||||||||||||||||
|
Pa-80 combination Pa-80結合 |
高鋁質鋼釬維增強耐火澆注料Hight Alumina sted fibre stre-nthend Refract-ory Castable | PA-80b | 1450 | ≥2.55 | ≥75 | / | ≥4 | ≥5 | / | ≥70 | ≥65 | / | ±0.50 | / | 膠水13-17glue | 搗打或振動RarnmingVibration |
窯口、冷卻機、噴煤管等及其它工業窯爐內襯的整體施工或修補 Nosering,cooler coal in-jection pipes and lining of kiln,entire construc-tion or local repait |
||||||||||||||||||||
|
Hight Temperature High-Alumin 高強高鋁 |
噴煤管專用自流高鋁低水泥澆注料 Semi self folwing high alumina low cement castable only usd for coal lngection pipes |
ZJ-16p | 1650 | ≥2.70 | ≥82 | ≤9 | ≥8 | ≥10 | ≥12 | ≥80 | ≥100 | ≥120 | ±0.30 | ±0.40 | 6-7 |
振動 Vibration |
噴煤管專用 For coal injection pipe only |
||||||||||||||||||||
|
窯口專用高鋁低水泥澆注料 Hight alumina low cement castable only used for nosering |
ZJ-16K | 1600 | ≥2.70 | ≥80 | ≤10 | ≥10 | 12 | ≥14 | ≥100 | ≥100 | ≥120 | ±0.40 | ±0.40 |
振動 Vibration |
窯口專用 For Nosering only |
||||||||||||||||||||||